以4,4′-二(4-氯甲酰基苯氧基)二苯砜(SODBC)与4,4′-二苯氧基二苯砜(DPODPS)、4,4′-二(2-甲基苯氧基)二苯砜(o-Me-DPODPS)、4,4′-二(3-甲基苯氧基)二苯砜(m-Me-DPODPS)和4,4′-二(2,6-二甲基苯氧基)二苯砜(o-Me2-DPODPS)等为单体在1,2-二氯乙烷(DCE)、N-2-甲基吡咯烷酮(NMP)、无水三氯化铝(AlCl3)溶剂催化剂体系中,通过低温溶液亲电共缩聚合成了聚芳醚砜醚酮(PESEK),邻位、间位甲基取代、双邻位甲基取代的聚芳醚砜醚酮(o-Me-PESEK、m-Me-PESEK、o-Me2-PESEK)聚合物.用FT-IR、1H NMR、DSC、TGA、WAXD等对聚合物进行了表征,研究了聚合物的溶解性.结果表明:聚合物具有较高的玻璃化转变温度(Tg)、良好的热稳定性和优良的溶解性.
A series of poly（arly ether sulfone ether ketone）s containing pendant methyl groups were synthesized by the reaction of 4,4′-[sulfonylbis（1,4-phenylene）dioxy]dibenzoyl chloride with 4,4′-diphenoxy diphenylsulfone （DPODPS）, 4,4′-di（2-methylphenoxy）dlphenylsulfone（o-Me-DPODPS）, 4,4′-di（3-methylphenoxy） diphenylsulfone （m-Me-DPODPS）, 4,4′-di（2,6-bimethylphenoxy） biphenylsulfone（o-Me2-DPODPS） respectively, in a mixture of 1,2-dichloroethane（DCE） and N-methylpyrrolidone （NMP）. These reactions were catalyzed by anhydrous aluminum chloride （AlCl3）. The characteristic of eopolymers were studied by means of advanced analytical techniques such as FT-IR,^ IH NMR, DSC, TGA and WAXD.The results show that glass transition temperature （Tg） in the range of 193-206℃, thermally stable in excess of 434 ℃ and excellent solubility in polar solvents.Methyl-substituted poly（aryl ether sulfone ketone）s had higher glass transition temperatures, lower initial decomposition temperatures than the unsubstituted ones.
出处
《江西师范大学学报（自然科学版）》
CAS
北大核心
2011年第4期331-334,共4页
Journal of Jiangxi Normal University(Natural Science Edition)
基金
"十一五"军品配套项目(JPPT-115-643)
国家自然基金青年科学基金(51003044)
江西师范大学青年成长基金资助项目
关键词
聚芳醚砜醚酮
甲基侧基
合成
结构与性能
poly（aryl ether sulfone ether ketone）
methyl pendent
synthesis
structure and property