摘要
对挤压后的Al⁃9.2Zn⁃2.4Mg⁃1.5Cu合金进行固溶时效处理,其中时效处理在水热环境下完成。采用光学显微镜、扫描电镜、显微硬度计和万能材料试验机等研究了各状态下合金的微观组织和力学性能。结果表明,Al⁃9.2Zn⁃2.4Mg⁃1.5Cu铝合金挤压板经固溶后合金未发生再结晶,晶粒仍呈纤维状,但晶内出现大量亚晶结构,且随着固溶温度的升高,亚晶结构数量也在增加。其次,由于合金Zn含量较高,均匀化后仍残留较多低熔点T相,挤压后低熔点T相沿挤压方向呈链状分布,固溶后部分低熔点T相回溶。当合金固溶温度为475℃时,水热环境下随着时效时间的增加,合金的抗拉强度先增加随后减小,水热时效时间10 h时达到峰值,其抗拉强度为733.53 MPa,屈服强度为694.83 MPa,伸长率为13.00%。
The Al⁃9.2Zn⁃2.4Mg⁃1.5Cu aluminum alloy after extrusion was solution treated and aged,where the aging was completed in hydrothermal environment.The microstructure and mechanical properties of the alloy were studied by optical microscope,scanning electron microscope,microhardness tester and universal material tester.The results show that there is no recrystallization in the Al⁃9.2Zn⁃2.4Mg⁃1.5Cu aluminum alloy extrusion sheet after solution treatment,and the grains are still fibrous,though in which there are a lot of subgrain structures and the number of subgrains increases with the increase of solution treatment temperature.Secondly,due to the high content of Zn in the alloy,there are still more low⁃melting point T phase remaining after homogenization.After extrusion,the low⁃melting point T phase is distributed in chains along the extrusion direction,and part of the low⁃melting point T phase redissolves after solution treatment.When the solution treatment temperature is 475℃,the tensile strength of the alloy increases first and then decreases with the increase of aging time in hydrothermal environment,the hydrothermal aging time for the peak of the alloy is 10 h,the tensile strength is 733.53 MPa,the yield strength is 694.83 MPa,and the elongation is 13.00%.
作者
刘阳
亓海全
秦翔智
韩向楠
李天然
Liu Yang;Qi Haiquan;Qin Xiangzhi;Han Xiangnan;Li Tianran(School of Materials Science and Engineering,Guilin University of Technology,Guilin Guangxi 541000,China;Kunshan Jingwei New Material Research Institute Co.,Ltd.,Kunshan Jiangsu 251301,China)
出处
《金属热处理》
CAS
CSCD
北大核心
2024年第2期166-171,共6页
Heat Treatment of Metals